NH2829

Description of NH2829GR

NH2829 New Material

NH2829 High Cost Effective New Material is a high-performance heat-resistant alloy independently developed by Qingdao NPA Industrial Co., Ltd. It has obtained a national invention patent (ZL202311060407.9). Through solid solution strengthening and second phase particle strengthening, NH2829 alloy exhibits excellent comprehensive properties, as well as good long-term microstructure and performance stability; By optimizing the composition design, nickel resources are saved, and the cost-effectiveness is higher. It can completely replace alloys such as Cr28Ni48W5 to make furnace rollers, radiation tubes, and other components, which can be applied in high-temperature and corrosive environments to meet the long-term stable operation needs of high-temperature equipment. It can not only create greater value for the industry, but also promote low-carbon environmental protection and energy green in society.

Basic Performance

Basic properties of NH2829 new material

Microstructure

The NH2829 alloy is mainly composed of Cr, Ni, and W alloying elements, with the addition of microalloying elements such as Co and Nb. Its microstructure consists of an austenitic matrix and NbC (white) and Cr ₇ C ∝ (gray) carbides.

High temperature strength

At high temperatures of 1000 ℃ and 1100 ℃, the tensile strength and yield strength of the Cr28Ni48W5 alloy are significantly better than those of the traditional Cr28Ni48W5 alloy. The specific data are as follows.

Hardness

Hardness is an important indicator for measuring the wear resistance and anti-adhesion capabilities of an alloy. Through solid solution strengthening by W and Co elements, and dispersion strengthening by NbC and Cr₇C₃ second-phase particles, the hardness of the NH2829 alloy is significantly improved. The Brinell hardness of the NH2829 alloy is more than 25% higher than that of Cr28Ni48W5. This higher hardness effectively resists the adhesion and wear of oxide scale and foreign matter on the component surface, reduces the formation of deposits, extends the wear life of the component, and lowers maintenance costs.

High temperature endurance performance

In terms of high-temperature durability, the durability life under the same conditions is better than that of Cr28Ni48W5.

The creep elongation under the same conditions is about one-third of that of Cr28Ni48W5 alloy, and its bending resistance is superior.

Material Comparison

Comparison between NH2829 alloy and traditional Cr28Ni48W5 alloy

In high-temperature industrial scenarios, components such as furnace rollers and radiation tubes have strict requirements for the mechanical properties of materials, and furnace rollers have high requirements for anti caking and anti bending performance. Compared with traditional heat-resistant alloy Cr28Ni48W5, NH2829 alloy has better core mechanical properties and lower cost advantages, with significant comprehensive competitiveness.

Properties Comparison	Cr28Ni48W5 Alloy	NH2829 Alloy
Hardness	Low hardness results in poor resistance to adhesion and abrasion from scale and foreign matter	Achieves a hardness of 226 HB, which effectively weakens the adhesion of oxide scale and foreign particles, thereby significantly reducing the risk of nodulation
Mechanical Strength	Its high-temperature strength is insufficient to meet the demands of long-term service under harsh conditions	The high-temperature mechanical properties are significantly enhanced, ensuring long-term service stability
High-Temperature Stress-Rupture and Creep Properties	Limited long-term load-bearing capacity and deformation resistance at elevated temperatures	Enhanced bending resistance and significantly improved high-temperature load-bearing and anti-deformation capabilities